SUMRX4 wrote:
The pin really isn't holding any weight. I towed an 8,000Lb tractor on a flatbed trailer about 60 miles once and after the trip I realized I never put the pin into the hitch. Won't do that again but that taught me the pin isn't doing any work.
valhalla360 wrote:mosseater wrote:
Any idea what the shear forces required to chop it in two? There are anomalies in this world but betting the farm very few ever are sheared. The receiver welds would probably fail before that pin would shear. I'd sooner keep the one I have road tested than risk a new one these days.
5/8inch pin has a cross sectional area of around 0.30in^2.
It will depend on the specific steel but say we made one of iron (not steel for a worst case scenario). Iron has a shear strength of around 26,000PSI.
So each end of the pin would have a strength of around 7,800 but since both ends would have to shear to get a failure, 15,600lb.
A descent quality steel (nothing exotic) can be twice that shear strength.
Keep in mind, when you tow, you aren't lifting the weight of the trailer. The force needed to pull the trailer is a small fraction of the trailer weight. Even in a panic stop, the trailer would push the truck into a skid long before the force reached the weight of the trailer.
So long as there is no sign of damage or deformation, it should be fine.
Grit dog wrote:opnspaces wrote:
If the pin is smooth and undamaged I would leave it alone. I would replace it if it's showing signs of damage like maybe the receiver tube gouging into the surface of the pin.
A few weeks ago I noticed that a replacement pin for a 2 inch receiver is a whole $3 on Amazon. At that price I ordered a few extras since I have multiple hitches at home. I also keep an extra in the center console of the Suburban as a just in case.
Amazon
$3 Scamazon hitch pins are maybe not the best purchase…I’ll leave it at that.
Grit dog wrote:
^Nope, but those may be good numbers for aluminum or brass or something. Hence why there’s no such thing as an aluminum hitch pin. You could rip 15000lbs in half just puttin the wood to it pulling your camper out of the driveway. (Not literally but it likely would not make it to the first campground.)
Any good hitch pin and maybe even the cheap $3 ones is going to have a shear strength FAR greater. Take normal 36ksi yield mild steel (that’s tensile strength). Ultimate tensile is more like 50ksi. Round numbers and approx.
Hitch pins are or should be 50-60-80ksi steel and shear is about 80% of tensile.
The factor of safety is 5-10 or idk maybe more.
Now bending is a different story. And why those silly reducer inserts for the trucks with 2.5-3” hitches are a horrible solution to being cheap with your hitch stingers.
The insert creates a short bending moment in the hitch pin and can and will easily pretzel a hitch pin. (And Waller out the holes in your hitch receiver, generally prior to bending the pin.)
I’ve cut off numerous bent pins due to those stupid little accessories.
mosseater wrote:
Any idea what the shear forces required to chop it in two? There are anomalies in this world but betting the farm very few ever are sheared. The receiver welds would probably fail before that pin would shear. I'd sooner keep the one I have road tested than risk a new one these days.